Temperature Rise during Primer, Adhesive, and Composite Resin Photopolymerization of a Low-Shrinkage Composite Resin under Caries-Like Dentin Lesions.

齲蝕様の象牙質病変の下の低収縮複合レジンのプライマー、接着剤と複合レジン光重合の間の体温上昇。

Published date

2012-12-24

Author

Sayed-Mostafa Mousavinasab, Maryam Khoroushi, Mohammadreza Moharreri

Affiliation

Torabinejad Dental Research Center and Department of Operative Dentistry, School of Dentistry, Isfahan University of Medical Sciences, Isfahan 81746-73461, Iran.

Abstract

Objective. This study evaluated temperature rise of low-shrinkage (LS) self-etch primer (P), LS self-etch adhesive (A), and P90 silorane-based composite resin systems, photopolymerized under normal and artificially demineralized dentin. Methods. Forty 1.5 mm-thick dentin discs were prepared from sound human molars, half of which were demineralized. Temperature rise was measured during photopolymerization using a K-type thermocouple under the discs: 10 s and 40 s irradiation of the discs (controls/groups 1 and 2); 10 s irradiation of primer (P), 10 s irradiation of adhesive (A), 40 s irradiation of P90 without P and A, and 40 s irradiation of P90 with P and A (groups 3 to 6, resp.). The samples were photopolymerized using an LED unit under 550 mW/cm(2) light intensity. Data was analyzed using repeated measures ANOVA and paired-sample t-test (α = 0.05). Results. There were no significant differences in temperature rise means between the two dentin samples for each irradiation duration (P > 0.0001), with significant differences between the two irradiation durations (P > 0.0001). Temperature rise measured with 40 s irradiation was significantly higher than that of 10 s duration for undemineralized and demineralized dentin P < 0.0001). Conclusions. Light polymerization of P90 low-shrinkage composite resin resulted in temperature rise approaching threshold value under artificially demineralized and undemineralized dentin.

 

目的本研究は低収縮(LS)自動エッチング・プライマー(P)の体温上昇を評価した、LSは接着剤(A)に自動エッチングする、そして、P90 siloraneベースの複合レジン系は正常なおよび人工的に脱鉱化された象牙質の下でphotopolymerizedした。
方法厚さ41.5mmの象牙質椎間板は健全なヒトの臼歯から準備された。
そして、それの半分は脱鉱化された。
体温上昇は、椎間板の下でKタイプ熱電対を用いて光重合の間、測定された:椎間板(対照/群1と2)の10sと40sの照射;プライマー(P)の10sの照射、接着剤(A)の10sの照射、PとAのないP90の40sの照射とPとA(群3~6、resp.)によるP90の40sの照射。
検体は、550mW/cm(2)の光度の下で、LED単位を用いてphotopolymerizedされた。
データは、反復手段分散分析と対応のある検体t検定(α= 0.05)を使用して分析された。
結果2つの照射期間(P > 0.0001)の間の有意差で、有意差が照射期間(P > 0.0001)ごとに、2つの象牙質検体の間に体温上昇手段の中になかった。
40sの照射で測定される体温上昇は、非脱鉱化されたおよび脱鉱化された象牙質のための10sの期間のそれより有意に高く、P < 0.0001であった)。
結論。
P90低収縮複合レジンの軽いポリメリゼーションは、人工的に脱鉱化されたおよび非脱鉱化された象牙質の下で限界値に近づいている体温上昇に帰着した。